Le papier "Polarity-Dependent Growth Rates of Selective Area Grown ZnO Nanorods by Chemical Bath Deposition" a été publié dans Langmuir

la-2017-00935n_0010.gif

la-2017-00935n_0010.gif

Ici  vous trouverez le papier de Thomas Cossuet

"Polarity is known to affect the growth and properties of ZnO single crystals and epitaxial films, but its effects are mostly unknown in ZnO nanorods. To leave polarity as the only varying parameter, ZnO nanorods are grown by chemical bath deposition under identical conditions and during the same run on O- and Zn-polar ZnO single crystals patterned by electron beam lithography with the same pattern consisting of 15 different domains. The resulting well-ordered O- and Zn-polar ZnO nanorod arrays with high structural uniformity are formed on all the domains. The comparison of their typical dimensions unambiguously reveals that Zn-polar ZnO nanorods have much higher growth rates than O-polar ZnO nanorods for all the hole diameter and period combinations. The distinct growth rates are explained in the framework of the surface reaction-/diffusive transport-limited elongation regime analysis, which yields a much larger surface reaction rate constant for Zn-polar ZnO nanorods. The origin of the difference is attributed to polarity-dependent dangling bond configurations at the top polar c-faces of ZnO nanorods, which may further be affected by polarity-dependent interactions with the ionic species in aqueous solution. These findings show the relevance of considering polarity as an important quantity in ZnO nanorods."

 



A+Augmenter la taille du texteA-Réduire la taille du texteImprimer le documentTélécharger au format PDFEnvoyer cette page par mail Partagez cet article Facebook Twitter Linked In Google+ Viadeo

Rédigé par David Munoz-Rojas

mise à jour le 14 juin 2017

  • Tutelle CNRS
  • Tutelle Grenoble INP
Communauté Université Grenoble Alpes
×
Afin d'améliorer la qualité de ce site et le service rendu à l'utilisateur, nous utilisons des cookies de mesure d’audience. En poursuivant votre navigation sur ce site, vous acceptez l'utilisation de cookies à cette fin. Pour en savoir plus