The paper "Effects of Mn3O4 precipitates on the vibrational properties of epitaxial Ca-doped LaMnO3 films" has been published in Journal of Physics D: Applied Physics

pap2.PNG

pap2.PNG

Here  you will find Michel Boudard's paper

"This work presents a systematic study by Raman spectroscopy of the vibrational properties of La0.7Ca0.3MnO3 (LCMO70/30) thin films epitaxially grown on LaAlO3 single crystalline substrates. The epitaxial LCMO70/30 thin films were prepared using a metal organic deposition process with thermal annealing at 800 °C, 900 °C and 1000 °C, with thicknesses ranging from 20–80 nm. The evolution of the Raman modes versus film thickness and annealing temperature have been investigated. The Raman spectra of the obtained films are found to be mainly dominated by three Raman lines at 225, 440 and 661 cm−1. The first two Raman lines are assigned to the vibrational modes of the LCMO70/30 films. However, by combining magnetization, x-ray diffraction and transmission electron microscopy with Raman spectroscopy, we concluded that the 661 cm−1 Raman line is due to the existence of a precipitate of a Mn3O4 phase in the LCMO70/30 films."


A+Augmenter la taille du texteA-Réduire la taille du texteImprimer le documentTélécharger au format PDFEnvoyer cette page par mail Partagez cet article Facebook Twitter Linked In Google+ Viadeo

Written by David Munoz-Rojas

Date of update October 19, 2017

Communauté Université Grenoble Alpes
×
To improve the quality of this site and the service rendered to the user, we use cookies audience measurement. By continuing your visit to this site, you agree to our use of cookies for this purpose. More